| Multifilament | Synthetic origin | Without dyeing |
Synthetic, absorbable, multifilament braided suture, in violet or undyed color.
Composed of a Polyglycolic acid with coated of polycaprolactone and calcium stearate.
The tissue reactivity in microscopic form is minimal.
The Absortion Is completed betwen 60 and 90 days the suture retains 70% of its original tensile streng in the second week
The material retains approximately 70% of its initial tensile strength by the end of two weeks.
Color code: Violet
Used in soft tissues coaptation, ligatures, and a wide variety of surgical specialties.
Retains 70% tensile strength at 2nd week and 50% tensile strength at 3rd week
Compositions :
The ATRAMAT® Polyglycolic Acid is coated with Poly(glicolide-co-lactide) (30/70) and Calcium Stearate (Violet) or with Polycaprolactone and Calcium Stearate (Undyed) in the following approximate percentages:
Polyglycolic Acid ......................... 99%
Coating .......................................... 1%
CHARACTERISTICS + BENEFITS
High tensile strength. = Excellent tissue support.
Braided structure. = Excellent handling.
Absorption through hydrolysis. = Predictable absorption rate and minimal tissue reaction
Cylindrical coated multifilament thread. = Smooth passage through the tissue.
Excellent knot coupling. = Providing excellent security.
Gauge within U.S.P./E.P. guidelines = Less suture material implanted in the tissue.
Hermetically sealed packaging = Ensure stability and sterility of the product.
ABOUT:
When implanted in the tissue, the ATRAMAT® Polyglycolic Acid has minimal tissue reaction on a microscopic basis. This is comparable to other absorbable synthetic sutures of Polyglycolic Acid. However, ATRAMAT® Polyglycolic Acid, offers a predictable absorption rate and high tensile strength over and above the USP standard, thus providing vital artificial support to the tissue during the critical healing period. The absorption occurs through progressive hydrolytic action completed in approximately 60 to 90 days. The material retains approximately 70% of its initial tensile strength at the end of the second week.
Retains 70% tensile strength at 2nd week and 50% tensile strength at 3rd week
Atramat® PGA
| Multifilament | asal sintetis | Tanpa pencelupan |
Sintetis, diserap, multifilament dikepang jahitan, di violet atau warna undyed.
Terdiri dari asam Polyglycolic dengan dilapisi dari polikaprolakton dan kalsium stearat.
Reaktivitas jaringan dalam bentuk mikroskopis minimal.
The Serapan Apakah selesai betwen 60 dan 90 hari jahitan mempertahankan 70% dari tarik streng aslinya di minggu kedua
Materi yang mempertahankan sekitar 70% dari kekuatan tarik awal pada akhir dua minggu.
Kode Warna: Violet
Digunakan coaptation lunak jaringan, ligatures, dan berbagai spesialisasi bedah.
Mempertahankan kekuatan tarik 70% pada minggu ke-2 dan kekuatan tarik 50% pada minggu ke-3
komposisi:
The ATRAMAT® Polyglycolic Asam dilapisi dengan Poli (glicolide-co-laktida) (30/70) dan Kalsium Stearate (Violet) atau dengan polikaprolakton dan Kalsium Stearate (undyed) dalam persentase perkiraan berikut:
Asam Polyglycolic ......................... 99%
Coating .......................................... 1%
KARAKTERISTIK + MANFAAT
Kekuatan tarik tinggi. = Dukungan jaringan yang sangat baik.
Struktur dikepang. = Penanganan yang sangat baik.
Penyerapan melalui hidrolisis. = Tingkat penyerapan diprediksi dan reaksi jaringan minimal
Silinder benang multifilamen dilapisi. = Bagian halus melalui jaringan.
Sangat baik simpul kopling. = Memberikan keamanan yang sangat baik.
Gauge dalam U.S.P. / E.P. pedoman = Kurang jahitan bahan ditanamkan dalam jaringan.
Tertutup rapat kemasan = Pastikan stabilitas dan sterilitas produk.
TENTANG:
Ketika ditanamkan dalam jaringan, yang ATRAMAT® Polyglycolic Asam memiliki reaksi jaringan minimal secara mikroskopis. Hal ini sebanding dengan jahitan sintetis diserap lainnya Asam Polyglycolic. Namun, ATRAMAT® Polyglycolic Asam, menawarkan tingkat penyerapan diprediksi dan kekuatan tarik tinggi di atas dan di atas standar USP, sehingga memberikan dukungan buatan penting untuk jaringan selama masa penyembuhan kritis. Penyerapan terjadi melalui aksi hidrolitik progresif selesai pada sekitar 60 sampai 90 hari. Materi yang mempertahankan sekitar 70% dari kekuatan tarik awal pada akhir minggu kedua.
Mempertahankan kekuatan tarik 70% pada minggu ke-2 dan kekuatan tarik 50% pada minggu ke-3
Galeri Foto :
Tidak ada komentar:
Posting Komentar