Synthetic, absorbable, monofilament suture, presented in violet color or undyed.
Made of a copolymer of glicolide and epsilon caprolactone.
The tissue reactivity is minimal.
Absorption occurs through progressive hydrolysis action; completed between 90 and 120 days.
The material retains approximately 60% of its initial tensile strength by the first week.
Color code: Soft Orange.
Frequently used in soft tissue coaptation.
Composition :
The ATRAMAT® PGC25 is a copolymer of glicolide and Epsilon-caprolactone in the following approximate percentages:
Polyglycolic Acid ..........................75%
Polycaprolactone ......................... 25%
CHARACTERISTICS + BENEFITS
High tensile strength = Excellent tissue support.
Absorption through hydrolysis = Predictable absorption rate and minimal tissue reaction
Monofilament with uniform diameter = Smooth passage through the tissue.
Excellent knot coupling = Providing excellent security.
Violet color = Excellent visiblity in the operating theatre.
Hermetically sealed packaging = Ensures stability and sterility of the product.
ABOUT:
Indicated for general approximation of soft tissue.
KNOTTING:When used with thick gauges (1, 0, 2-0 USP) it is preferable to tie both a surgeon knot and simple knot. This will allow the surgeon to adjust the tension accordingly. An additional square knot is recommended according to the surgical circumstances and the surgeon experience.
When applied in thin gauges (3-0, 4-0, 5-0, 6-0 USP), initially two square knots are recommended with 2 or 3 additional throws, leaving the ends of the knots 4 to 5 mm long subject to the surgical circumstances and the surgeon experience. Damaging the suture thread with forceps, needle holders and so on, should be avoided.
Retains 60% (violet thread) 50% (non-dyed thread) tensile strength at 1st week and 30% (Violet thread) 20% (non-dyed thread) tensile strength at 2nd week
Monofilamen | asal sintetis | Tanpa pencelupan |
Sintetis, diserap, monofilamen jahitan, disajikan dalam warna violet atau undyed.
Terbuat dari kopolimer glicolide dan epsilon kaprolakton.
Reaktivitas jaringan minimal.
Penyerapan terjadi melalui aksi hidrolisis progresif; selesai antara 90 dan 120 hari.
Materi yang mempertahankan sekitar 60% dari kekuatan tarik awal pada minggu pertama.
Kode warna: Lembut Orange.
Sering digunakan dalam coaptation jaringan lunak.
Komposisi:
The ATRAMAT® PGC25 adalah kopolimer glicolide dan Epsilon-kaprolakton dalam persentase perkiraan berikut:
Asam Polyglycolic .......................... 75%
Polikaprolakton ......................... 25%:
KARAKTERISTIK + MANFAAT
Kekuatan tarik tinggi = dukungan jaringan yang sangat baik.
Penyerapan melalui hidrolisis = tingkat penyerapan diprediksi dan reaksi jaringan minimal
Monofilamen dengan seragam diameter = bagian halus melalui jaringan.
Sangat baik simpul kopling = Memberikan keamanan yang sangat baik.
Warna violet = sangat baik visiblity dalam ruang operasi.
Tertutup rapat kemasan = Memastikan stabilitas dan sterilitas produk.
TENTANG:
Diindikasikan untuk pendekatan umum jaringan lunak.
Knotting: Jika digunakan dengan alat pengukur tebal (1, 0, 2-0 USP) adalah lebih baik untuk mengikat kedua simpul ahli bedah dan simpul sederhana. Hal ini akan memungkinkan ahli bedah untuk menyesuaikan ketegangan sesuai. Sebuah simpul persegi tambahan dianjurkan sesuai dengan keadaan bedah dan pengalaman ahli bedah.
Bila diterapkan dalam pengukur tipis (3-0, 4-0, 5-0, 6-0 USP), awalnya dua knot persegi direkomendasikan dengan 2 atau 3 tambahan melempar, meninggalkan ujung simpul 4 sampai 5 mm tunduk keadaan bedah dan pengalaman ahli bedah. Merusak benang jahit dengan forceps, pemegang jarum dan sebagainya, harus dihindari.
Mempertahankan 60% (violet benang) 50% (non-dicelup benang) kekuatan tarik pada minggu 1 dan 30% (Violet benang) 20% (non-dicelup benang) kekuatan tarik pada minggu ke-2